High cycle fatigue tests at a constant positive mean stress have been performed on a Al-Si-Cu cast aluminum alloy. The Random Fatigue Limit (RFL) model was employed to fit the probabilistic S-N curves based on Maximum Likelihood Estimate (MLE). Fractographic studies indicated that fatigue cracks in most specimens initiate from oxide films located at or very close to specimen surface. The RFL model was proved to be able to accurately capture the scatter in fatigue life. The cumulative density function (CDF) of fatigue life determined by RFL fit is found to be approximately equal to the complementary value of the CDF of the near-surface fatigue initiator size.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Correlation between Scatter in Fatigue Life and Fatigue Crack Initiation Sites in Cast Aluminum Alloys


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Engler-Pinto, Carlos (Autor:in) / Cui, Haitao (Autor:in) / Wen, Weidong (Autor:in) / Zheng, Xin (Autor:in) / Su, Xuming (Autor:in)

    Kongress:

    SAE 2012 World Congress & Exhibition ; 2012



    Erscheinungsdatum :

    2012-04-16


    Format / Umfang :

    7 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Fatigue life scatter of aluminum alloy helicopter lugs

    Xi, N.S. / Xie, M.L. / Zhang, Z.L. et al. | Tema Archiv | 2000



    Fatigue crack initiation life prediction of railroad wheels

    Liu, Yongming / Stratman, Brant / Mahadevan, Sankaran | Tema Archiv | 2006


    Elastomeric Component Fatigue Analysis: Rubber Fatigue Prediction and Correlation Comparing Crack Initiation and Crack Growth Methodologies

    Chandrashekar, Ravish / Bodombo Keinti, Robert / Datta, Sandip et al. | SAE Technical Papers | 2020


    Fatigue crack propagation in aerospace aluminum alloys

    Gangloff, Richard P. / Piascik, Robert S. / Dicus, Dennis L. et al. | AIAA | 1994