Stress-relief annealing is an indispensable processing step for non-oriented electrical steel (NOES) sheets to achieve optimal magnetic properties. The annealing microstructure and texture are not only dependent on the annealing conditions, but also on the prior thermomechanical processing history. To investigate the effect of deformation mode on the recrystallization behavior, a NOES containing 0.9 wt% Si was cold rolled by skew rolling in which the hot-rolled-and-annealed plate was fed at 45° into the rolls to change both the initial texture and the deformation mode. The skew-cold-rolled sheets and those rolled by conventional and cross rolling were then annealed at different temperatures (650 to 1050 °C) for different times (0.5 to 30 min). The recrystallization behavior was characterized using electron backscatter diffraction (EBSD) techniques. It was found that the cold rolling deformation mode and the initial texture have a significant effect on the recrystallization behavior. The recrystallization rates of the skew- and cross- rolled sheets are higher than that of conventionally rolled steel if the annealing temperature is low (650 °C) or the annealing time is short (0.5 min). When the annealing temperature is relatively high (850 °C) and the annealing time is relatively long (2 min), the difference in recrystallization rate is small. In all the cases, skew rolling promotes the formation of the desired <001>//ND (normal direction) texture, and the unfavorable <111>//ND texture is essentially eliminated.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Recrystallization Behavior of Non-oriented Electrical Steel Sheets after Skew Cold Rolling


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Sanjari, Mehdi (Autor:in) / He, Youliang (Autor:in)

    Kongress:

    WCX SAE World Congress Experience ; 2023



    Erscheinungsdatum :

    2023-04-11




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Recrystallization texture of Si-containing cold rolled high strength steel sheets

    Sudo, M. / Hashimoto, S. / Kanbe, S. | Tema Archiv | 1980


    Effect of Edge Finish on Fatigue Behavior of Thin Non-oriented Electrical Steel Sheets

    Behravesh, Behzad / Saha, Dulal / Lamonaca, Gianni et al. | SAE Technical Papers | 2023


    125 years of skew rolling

    Online Contents | 2010


    Ni-Al intermetallics obtained by cold-rolling elemental metal sheets

    Battezzati, L. / Antonione, C. / Fracchia, F. et al. | British Library Conference Proceedings | 1994


    Ni-Al intermetallics obtained by cold-rolling elemental metal sheets

    Battezzati,L. / Antonione,C. / Fracchia,F. et al. | Kraftfahrwesen | 1994