Electron microscopy and microprobe analysis were used to study the spread of corrosion beneath an acrylic paint film on steel. Corrosion initiates beneath the paint film in crevices formed by scribing. Corrosion spreads as the build up of corrosion products beneath the paint film drives a crack along the paint/substrate interface. The buildup of corrosion products cause defects to form in the paint film. Phosphating reduces the corrosion rate by increasing the polymer/substrate adhesion and slowing down crack growth at the interface. The improved adhesion can be explained in terms of acid-base interactions between the polymer and substrate. Sulfur was identified in the corrosion products of the one sample which was studied. The sulfur is presumed to be from atmospheric pollutants.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Atmospheric Corrosion Mechanisms of Painted Steel


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1983



    Erscheinungsdatum :

    01.02.1983




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Atmospheric Corrosion Mechanisms of Painted Steels

    Standish,J.W. / Armco,Res.Cent.US | Kraftfahrwesen | 1983


    Electrochemical Study Of Corrosion Of Painted Steel

    Mendrek, M. H. / Higgins, R. H. / Danford, M. D. | NTRS | 1990


    Painted steel appearance

    Online Contents | 1993


    Painted steel appearance

    Kraftfahrwesen | 1993


    A cyclic model of cosmetic corrosion for painted steel sheets

    Schmitz,B. / Defourny,J. / Leroy,V. et al. | Kraftfahrwesen | 1993