Sliding wear characteristics of ceramic matrix composites (CMC) produced by the directed metal oxidation process(*) were evaluated using a block-on-ring wear test machine at 75-85°C under lubricated conditions. The ceramic matrix composite consisted of silicon carbide particulate in an aluminum oxide matrix that also contained a small amount of metal. For comparison, wear characteristics of alumina, silicon carbide, sialon and silicon nitride were also determined. The blocks of the test materials were tested against rings of SAE 4140 steel heat treated to 57-59 Rockwell C hardness. The optimized CMC composition showed wear performance similar to those of the best ceramic materials, silicon nitride and sialon, and was far superior to that of the cast iron.The optimized CMC composition was also evaluated using a single cam wear tester (The Motor Industry Research Association (U.K.) tester) at various loads for up to 20 million cycles. The test load at which failure occurred was slightly higher than that for silicon nitride and chilled cast iron and was much higher than that for alumina (zirconia toughened alumina).These results indicate that ceramic matrix composites produced by the directed metal oxidation process may be attractive candidate materials for sliding followers.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Evaluation of Sliding Wear Characteristics of Ceramic Matrix Composites for Cam Followers


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Congress & Exposition ; 1993



    Erscheinungsdatum :

    1993-03-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Evaluation of tribological performance of ceramic roller followers

    Gangopadhyay,A. / Cheng,H.S. / Harman,S.T. et al. | Kraftfahrwesen | 1990


    Evaluation of Tribological Performance of Ceramic Roller Followers

    Gangopadhyay, Arup / Cheng, H. S. / Corwin, J. M. et al. | SAE Technical Papers | 1990


    Wear behaviour of A356/25SiCp aluminium matrix composites sliding against automobile friction material

    Natarajan, N. / Vijayarangan, S. / Rajendran, I. | Tema Archiv | 2006


    Evaluation of Mechanical Properties of Ceramic Matrix Composites

    Koch, D. / Tushtev, K. / Gaab, L. et al. | British Library Conference Proceedings | 2008