The standard tests for exhaust system materials are reviewed and new tests involving cyclic oxidation and salt exposure plus oxidation are suggested. The importance of edge oxidation in the interpretation of oxidation weight gain measurement for coated steels is demonstrated. For aluminum-coated steel Type 1, 80% of the weight gain was due to edge oxidation for the test conditions used. Depth profiling an oxidized aluminum-coated steel Type 1 shows why this product is an excellent material for elevated temperature applications. The protective oxide on the aluminum-coated product remains almost pure aluminum oxide even after the coating has alloyed with the base steel. Improved aluminum-coated steels are shown to be possible by changing the chemical composition of the steel substrate.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Aluminum-Coated Steels for Elevated Temperature Applications


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1981



    Erscheinungsdatum :

    1981-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Aluminium-coated steels for elevated temperature applications

    Gibson,A.F. / Kilbane,F.M. / Dunbar,F.C. et al. | Kraftfahrwesen | 1981


    Elevated Temperature Aluminum Alloys for Aerospace Applications

    Sakata, I. F. / Langenbeck, S. L. | SAE Technical Papers | 1983


    Elevated temperature aluminum alloys for aerospace applications

    Sakata, I.F. / Langenbeck, S.L. | Tema Archiv | 1983



    A high-strength and heatresistant aluminium coated steel for elevated temperature applications

    Kawase,H. / Yamada,T. / Nisshin Steel,Kure,JP | Kraftfahrwesen | 1989