In this study, to confirm the practical advantages and acceptability of galvannealed TS800MPa grade dual-phase steel (DP800), crashworthiness and spot weldability as important properties in practical use were investigated and compared with conventional galvannealed TS440MPa grade and microalloyed TS600MPa grade steels, which are currently used for frame parts. The results have shown that DP800 has high absorbed energy on crash tests, and has almost the same acceptable weldability as comparative steels.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Crashworthiness and Spot Weldability of Galvannealed DP800 Steel Sheet


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Kamura, M. (Autor:in) / Kawamoto, Y. (Autor:in) / Omiya, Y. (Autor:in) / Utsumi, Y. (Autor:in)

    Kongress:

    International Body Engineering Conference & Exhibition and Automotive & Transportation Technology Congress ; 2002



    Erscheinungsdatum :

    16.10.2001




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Crashworthiness and spot weldability of galvannealed DP800 steel sheet

    Kamura,M. / Utsumi,Y. / Omiya,Y. et al. | Kraftfahrwesen | 2002


    Improvements in Formabibity and Spot Weldability of Galvannealed Steel Sheet

    Yasuda, Akira / Kato, Chiaki / Mochizuki, Kazuo et al. | SAE Technical Papers | 1994


    Improvements on formability and spot weldability of galvannealed steel sheet

    Tobiyama,Y. / Yasuda,A. / Mochizuki,K. et al. | Kraftfahrwesen | 1994



    Spot-weldability of galvannealed steel sheets with a tensile strength of 590 MPa

    Sakuma,Y. / Takahashi,Y. / Nippon Steel,JP et al. | Kraftfahrwesen | 2002