As the geometric complexity and tolerance requirements of powder metal parts become more demanding added machining operations are required as a necessary step in the manufacturing process. Likewise, a better understanding of the effects powder metal materials and processes have on the machinability of P/M components is needed.An investigation into the effects of post-sintering cooling rate on the microstructure, machinability and tensile properties of an FC-0208 copper steel was conducted. Machinability was measured using a drill test on a high volume production component. Three cooling rates (9, 17 and 40 ° C/minute) were used to generate the variation in microstructure. Machinability analysis was performed using box-and-whisker plots and includes drill motor load, hole size on drill entry and exit, and microfinish. Metallography and tensile properties and a discussion of their relationship with machinability are included.Results indicate that the above mentioned cooling rates can produce a measurable difference in microstructure, machinability and tensile performance. A slow cooling rate can be employed to improve the machinability of this material. However, a substantial decrease in tensile properties results. Therefore, care must be taken to properly control the microstructure to optimize both machinability and mechanical properties for the application of interest.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Enhanced Machinability of P/M Parts Through Microstructure Control


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Congress & Exposition ; 1994



    Erscheinungsdatum :

    01.03.1994




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Enhanced Machinability of P/M Parts Through Microstructure Control

    Fulmer, J. J. / Blanton, J. M. / SAE | British Library Conference Proceedings | 1994


    Enhanced machinability of P/M parts through microstructure control

    Fulmer,J.J. / Blanton,J.M. / Burgess-Norton Manufacturing,US | Kraftfahrwesen | 1994


    Improvement of Machinability in PM Parts Using Manganese Sulfide

    Chopra, K. S. | British Library Conference Proceedings | 1998


    Machinability

    Schlesinger, G. | Engineering Index Backfile | 1936


    Machinability

    Engineering Index Backfile | 1945