The current investigation compares the friction behavior between specimens extracted from engine blocks of grey cast iron (class FC 250 ABNT NBR 6589 standard) and compacted graphite iron (class GJV450 ISO 16112 standard). The effect of wall thickness was evaluated, by extracting samples from regions equivalent to two levels of thickness. The piston ring used was a nitrided martensitic stainless steel with an asymmetric profile, and the lubricant oil was the SAE 30 CF. The tribological tests were conducted at 75 N normal load for a duration of 1 hour, a frequency of 5 Hz and a stroke of 10 mm. The tests were carried out at a controlled temperature of 40° C. In a general way, the compacted graphite irons presented smaller friction coefficients when compared to that observed for the lamellar ones; and the wall thickness showed relevance only for the compacted graphite iron, being the lowest values found for the thinner wall. On the other hand, for the grey cast iron, the wall thickness did not affect significantly the friction behavior. Finally, all materials presented a tendency to a smoothing of the surface after tests.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Evaluation of friction coefficient of lamellar and compacted graphite irons in lubricated ring-on-cylinder system


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    2018 SAE Brasil Congress & Exhibition ; 2018



    Erscheinungsdatum :

    2018-09-03




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Compacted Graphite Irons - High Quality Engineering Materials in the Cast Iron Family

    Hughes, I. C. H. / Powell, J. | SAE Technical Papers | 1984


    Cylinder irons

    Hurst, J.E. | Engineering Index Backfile | 1933


    Compacted Graphite Irons - High Quality Engineering Materials in the Cast Iron Family

    Hughes,I.C. / Powell,J. / Alvechurch,GB | Kraftfahrwesen | 1984


    Piston and cylinder irons

    Knittel, R. | Engineering Index Backfile | 1934


    Sliding Wear Behavior of Compacted Graphite Iron Cylinder Liner Material

    Prasad, M. Sathya / Dhanasekaran, S. / Sharma, Samir et al. | SAE Technical Papers | 2014