In this study, reaction path analysis and modeling of NOx reduction phenomena by fast SCR reaction on a Cu-chabazite catalyst were conducted, considering the formation and decomposition of ammonium nitrate (NH4NO3). White crystals of NH4NO3 decompose at temperatures < 200 °C. Thus, the reaction behavior changes at 200 °C under fast SCR reaction conditions. NH4NO3 formation can occur on both Cu sites and Brønsted acid sites, which are active sites for NOx reduction in the Cu-chabazite catalyst, but it is unclear where NH4NO3 accumulates on the catalyst. Analyses using catalyst test pieces with different active sites were performed to estimate this accumulation. The results suggested that NH4NO3 accumulation does not depend on the presence of either Cu sites or Brønsted acid sites. Therefore, it is assumed that NH4NO3 can be accumulated everywhere on the catalyst, including on the zeolite framework. This phenomenon was included in the model as formation/accumulation sites S'. As a result, a model considering the fast SCR reaction behavior changes under 200 °C was developed. Validation results confirmed that the model could accurately predict NOx reduction phenomena for a wide range of temperatures and NO2/NOx ratios. The results also suggested that the model was applicable under transient conditions of NH3 concentration. The model performed well under a wide range of conditions by considering active sites and reactions on the catalyst.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Reaction Analysis and Modeling of Fast SCR in a Cu-Chabazite SCR Catalyst Considering Generation and Decomposition of Ammonium Nitrate


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Kusaka, Jin (Autor:in) / Seki, Keiichiro (Autor:in) / Ogawa, Kenya (Autor:in) / Oka, Kohei (Autor:in) / Sok, Ratnak (Autor:in) / Ueyama, Rikuto (Autor:in) / Tsukamoto, Yoshihisa (Autor:in)

    Kongress:

    15th International Conference on Engines & Vehicles ; 2021



    Erscheinungsdatum :

    2021-09-05




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Formation and Decomposition of Ammonium Nitrate on an Ammonia Oxidation Catalyst

    Ottinger, Nathan / Xi, Yuanzhou / Liu, Z. Gerald | SAE Technical Papers | 2018


    Ammonium Nitrate Formation and Decomposition on an Extruded Vanadium-Based SCR Catalyst

    Keturakis, Christopher / Ottinger, Nathan / Xi, Yuanzhou et al. | SAE Technical Papers | 2020


    Impact of Hydrothermal Aging on the Formation and Decomposition of Ammonium Nitrate on a Cu/zeolite SCR Catalyst

    Keturakis, Christopher / Ottinger, Nathan / Xi, Yuanzhou et al. | SAE Technical Papers | 2017


    Improvement of Catalytic Decomposition of Ammonium Nitrate with New Bimetallic Catalysts

    Farhat, Kamal / Cong, Weimin / Batonneau, Yann et al. | AIAA | 2009