The morphology of salt water stress corrosion cracks in 8A1-1Mo-1V titanium alloy has been determined. In the interior of the specimens the cracks are brittle in nature and far more extensive than indicated by cracks visible at the specimen surface. The direction of propagation of the internal cracks is away from the plane of the specimen starter crack. These crack characteristics are explained in terms of internal stress state and presence of contaminants containing chlorides.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Effect of Chloride Contamination on Cracking in Titanium


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Cowgill, D. S. (Autor:in) / Fritzen, J. S. (Autor:in) / Weber, K. E. (Autor:in) / Krystkowiak, S. (Autor:in)

    Kongress:

    National Aeronautic and Space Engineering and Manufacturing Meeting ; 1968



    Erscheinungsdatum :

    1968-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Stress corrosion cracking of titanium alloys.

    BECK, T. R. / BLACKBURN, M. J. | AIAA | 1968


    STRESS CORROSION CRACKING OF TITANIUM ALLOYS

    BECK, T. / BLACKBURN, M. | AIAA | 1967


    Stress corrosion cracking of titanium alloys.

    Beck, T. R. / Blackburn, M. J. | NTRS | 1968