Fracture toughness tests were conducted on the SAEFDE Committee's round-robin A356-T6 cast aluminum alloy materials designated X, Y and Z. Compact type specimens with a thickness of 9.1 and 20.3 mm were tested. Valid Klc values couid not be obtained for 9.1 mm thick specimens but were obtained for 20.3 mm thickness specimens. Due to larger castings, and hence slower cooling rates, a coarse secondary dendrite arm spacing, DAS, of 80 to 90 μm existed in the three materials. Similar Klc values were 18, 16.7 and 17.3 for the A356-T6 materials X, Y and Z respectively. Final fracture surfaces were also similar with predominant cleavage fracture with some localized ductile dimples and secondary cracking.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fracture Toughness of A356-T6 Cast Aluminum Alloy


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Stephens, R. I. (Autor:in) / Koh, S. K. (Autor:in)

    Kongress:

    SAE International Congress and Exposition ; 1988



    Erscheinungsdatum :

    01.08.1988




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fatigue and Fracture Toughness of Water-Chilled A356-T6 Cast Aluminum Alloy

    Mahoney, B. J. / Stephens, R. I. | SAE Technical Papers | 1988


    Low Cycle Fatigue of A356-T6 Cast Aluminum Alloy

    Wigant, C. C. / Stephens, R. I. | SAE Technical Papers | 1987


    Low cycle fatigue of A356-T6 cast aluminum alloy

    Wigant,C.C. / Stephens,R.I. / Univ.of Iowa,US | Kraftfahrwesen | 1987


    Fatigue Crack Growth of A356-T6 Cast Aluminum Alloy

    Wigant, C. C. / Stephens, R. I. | SAE Technical Papers | 1988


    Low Cycle Fatigue of A356-T6 Cast Aluminum Alloy Wheels

    Mahoney, B. J. / Fossman, R. G. / Stephens, R. I. | SAE Technical Papers | 1988