Tensile tests were performed on DP600 and DP780 dual-phase steels to determine the relative effects of bake-hardening on the static and dynamic material response. The quasi-static test variables were prestrain level, specimen orientation (longitudinal, transverse), and heat treatment (as-received, bake hardened). Dynamic tests were performed at rates ranging from 0.001/s to 500/s, with variables of prestrain level and heat treatment. Increases in the ultimate and yield strength for both DP600 and DP780 were mainly due to prestrain and strain rate effects. The bake-hardening effects varied with the material, amount of prestrain, and strain rate. Crush tests were also performed on DP780 tubes in the as-received and bake-hardened conditions at rates ranging from quasi-static up to 7250 mm/s. The energy absorption was similar regardless of the rate.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Bake-Hardening Effect of Dual Phase Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Belwafa, Jamel (Autor:in) / Wang, Kangping (Autor:in) / Kuhlman, Sarah H. (Autor:in) / Hill, Susan I. (Autor:in) / Chen, Xiaoming (Autor:in)

    Kongress:

    SAE World Congress & Exhibition ; 2009



    Erscheinungsdatum :

    20.04.2009




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Dent-resistant bake-hardening steels for automotive outer-body applications

    Pradhan,R. / Bethlehem Steel,US | Kraftfahrwesen | 1991


    Dent-resistant bake-hardening steels for automotive outer-body applications

    Pradhan,R. / Bethlehem Steel,US | Kraftfahrwesen | 1990


    Bake Hardening Behavior of Advanced High Strength Steels under Manufacturing Conditions

    Kantereit, H. / Society of Automotive Engineers | British Library Conference Proceedings | 2011