In this research, the aim is to investigate the tensile properties and microstructures of Aluminium 6061 hybrid composite before and after extrusion. Aluminium 6061 Hybrid composite was fabricated using Stir casting technique with 6 Weight % silicon nitride (Si3N4) coated with nickel and 1Weight % carbon fiber (Cf) coated with copper as reinforcements followed by extrusion process. The tensile properties and microstructures of extruded hybrid composite was investigated and compared with as-cast hybrid composite. The microstructure of the hybrid composite showed excellent bonding between matrix and reinforcements interface. The hot extruded hybrid composite exhibited enhanced yield strength (44%), ultimate tensile strength (33%) and % elongation (20%) when compared with as-cast hybrid composite. Scanning electron microscopy (SEM) and Energy dispersive spectroscopy (EDS) techniques were used to observe the fracture surfaces of tensile testing specimens.
Influence of Hot Extrusion Process on Tensile Properties and Microstructures of Aluminium 6061 Hybrid Composite
Sae Int. J. Adv. and Curr. Prac. in Mobility
2023 AeroTech ; 2023
Sae International Journal of Advances and Current Practices in Mobility ; 5 , 5 ; 1834-1840
2023-03-07
7 pages
Aufsatz (Konferenz)
Englisch
Microstructures, Tensile Properties and Forming Process of AZ31 Alloy Sheets
British Library Conference Proceedings | 2007
|Influence of Heat Treatment of Aging on the Mechanical Properties of Aluminium 6063 T5 AND 6061 T6
British Library Conference Proceedings | 2011
|Fatigue behavior of 6061-T6 aluminium alloy plain specimens
Kraftfahrwesen | 1997
|Tensile Properties of Large Extrusion and Forgings of RS P/M Al-9Fe-1.9Mo-1.7Si Aluminium Alloy
British Library Conference Proceedings | 2007
|Cracking Susceptibility and Joint Property Study of the 6061 Aluminium
British Library Conference Proceedings | 2007
|