The unnotched Charpy impact properties of carburized 8620, 4620, 4620 + 0.3 Mo, and 3310 were studied at two case depths. The ranking of the alloys in order of increasing impact strength for both case depths was: 8620, 4620, 4620 + 0.3 Mo, 3310. Increasing the nickel content of carburized steel resulted in greater crack initiation resistance in the carburized case. Increasing the molybdenum content, while maintaining the nickel content constant, increased the crack propagation resistance of the core material. Additional tests showed the amount of austenite which transformed prior to fracture and the fracture strain increased with nickel content. The greater amount of austenite transformed during straining before fracture results in the improved crack resistance of carburized cases of the high nickel steels.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Impact Properties of Selected Gear Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1978 SAE International Off-Highway and Powerplant Congress and Exposition ; 1978



    Erscheinungsdatum :

    01.02.1978




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Impact properties of selected gear steels

    Shea,M.M. / General Motors Res.Lab.,US | Kraftfahrwesen | 1978


    Gear steels

    Heldt, P.M. | Engineering Index Backfile | 1938


    Gear steels

    Heldt, P.M. | Engineering Index Backfile | 1938


    Impact Fatigue Resistance of Commonly Used Gear Steels

    DePaul, R. A. | SAE Technical Papers | 1971


    Corrosion of Landling Gear Steels

    Lee, E. U. / Kozol, J. / Boodey, J. B. et al. | British Library Conference Proceedings | 1995