A series of bending fatigue tests were conducted and S-N data were obtained for two groups of 4320 steel samples: (1) carburized, quenched and tempered, (2) carburized, quenched, tempered and shot peened. Shot peening improved the fatigue life and endurance limit. The S-N data exhibited large scatter, especially for carburized samples and at the high cycle life regime. Sample characterization work was performed and scatter bands were established for residual stress distributions, in addition to fracture and fatigue properties for 4320 steel. Moreover, a fatigue life analysis was performed using fracture mechanics and strain life fatigue theories. Scatter in S-N curves was established computationally by using the lower bound and upper bound in materials properties, residual stress and IGO depth in the input data. The results for fatigue life analysis, using either computational fracture mechanics or strain life theory, agreed reasonably well with the test data. However, the scatter in the fatigue properties of the material and the scatter in residual stress could not fully account for the large scatter in fatigue life. Other factors that might be considered for root causes of the observed large fatigue life scatter were identified and discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Investigation of S-N Test Data Scatter of Carburized 4320 Steel


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Matlock, David K. (Autor:in) / Krauss, George (Autor:in) / Fett, Gregory A. (Autor:in) / Lin, Hong (Autor:in) / Sanders, James A. (Autor:in) / Binoniemi, Robert R. (Autor:in)

    Kongress:

    SAE World Congress & Exhibition ; 2007



    Erscheinungsdatum :

    16.04.2007




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Investigation of S-N Test Data Scatter of Carburized 4320 Steel

    Lin, H. / Fett, G. A. / Binoniemi, R. R. et al. | British Library Conference Proceedings | 2007


    Investigation of s-n-test data scatter of carburized 4320 steel

    Lin,H. / Fett,G.A. / Sanders,J.A. et al. | Kraftfahrwesen | 2007


    Bending Fatigue Performance of Carburized 4320 Steel

    Matlock, David K. / Krauss, George / Cohen, Rachael E. | SAE Technical Papers | 1993


    Bending fatigue performance of carburized 4320 steel

    Cohen,R.E. / Krauss,G. / Matlock,D.K. et al. | Kraftfahrwesen | 1993


    Bending Fatigue Crack Characterization and Fracture Toughness of Gas Carburized SAE 4320 Steel

    Matlock, David K. / Krauss, George / Cohen, Rachael E. et al. | SAE Technical Papers | 1992