Thin film sensors are often used for in-situ measuring. They are composed of a sensor/conductor layer and insulation layers on either side. However, delamination often occurs between the insulation layers and the sensor/conductor layer and makes the sensor life span shorter. This problem is found especially when there is continuous stress caused by the cyclic change of temperature, sliding and tension. By observing the microstructure of the sensor with transmission electron microscope (TEM), it was found that the adhesion force at the interface between the insulation layer and the sensor/conductor layer, where delamination occurs, is not strong enough, because the interface is too flat. By deposition a thin insulator layer with rough surface on the normal insulation layer, the delamination was successfully suppressed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Investigation and Improvement of Interfacial Delamination in In-Situ Measuring Sensor for Automobile Application


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE 2013 World Congress & Exhibition ; 2013



    Erscheinungsdatum :

    2013-04-08




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Modeling Delamination in Composites via Continuum Interfacial Displacement Discontinuities

    Ranatunga, V. / Bednarcyk, B. / Arnold, S. | British Library Conference Proceedings | 2009


    Modeling Delamination in Composites via Continuum Interfacial Displacement Discontinuities

    Ranatunga, Vipul / Bednarcyk, Brett / Arnold, Steven | AIAA | 2009


    Enhancement to the Interfacial Element Formulation for the Prediction of Delamination

    Goyal, Vinay / Schubel, Patrick / Rome, Jacob et al. | AIAA | 2007



    Automobile Performance Improvement Device

    LEE RAE JIN | Europäisches Patentamt | 2019

    Freier Zugriff