A 50 kg/mm2 tensile strength level and an extremely high flangeability were achieved in a developed steel. The steel had a base chemistry of C=0.04%, Mn=0.85%, Nb=0.015%, and S=0.001%, and was processed with a hot rolling finishing temperature of 860 °C and a coiling temperature of 550 °C. This high flangeabilty was attained by reducing S content below 0.002%, as well as reducing carbon content. Elongation results could not be directly correlated to the flangeability of steel. A steel's flangeability has been found to be associated with microvoid distribution in the “as punched” condition. The developed steel exhibited the lowest density, and the smallest size, of microvoid.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of High Strength Hot Rolled Steel to Be Applied for Flanging Deformation


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    International Body Engineering Conference & Exposition ; 1998



    Erscheinungsdatum :

    1998-09-29




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Development of High Strength Hot Rolled Steel to Be Applied for Flanging Deformation

    Kobayashi, H. / SAE | British Library Conference Proceedings | 1998



    Evaluation of Metal Gainers for Advanced High Strength Steel Flanging

    Du, Changqing / Hsiung, Ching-Kuo / Roman, Chris et al. | SAE Technical Papers | 2014


    Present Status of Cold-Rolled High Strength Steel Development

    Klems, George J. / Malcolm Gray, J. | SAE Technical Papers | 1974


    High-Strength, Hot-Rolled Steel Bars

    SAE Technical Papers | 2003