In this work, the type and level of strain are related to the degree of corrosion resistance and the type of coating damage for three coatings: 40 gm/m2 electrogalvanized steel, 80 gm/m2 electrogalvanized steel and Zincroplex™, a zinc-rich paint over 40 gm/m2 electrogalvanized steel. The coating weight of the electrogalvanized steels was a factor in the degree of coating damage and thus affected corrosion resistance. The electrogalvanized steels were adversely affected by bi-axial deformation. Zincroplex™ failed under draw-type deformation. Although the corrosion limit diagram technique does not predict service life, it can distinguish among the capabilities of different materials at different levels and types of strain.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Corrosion Response of Electrogalvanized Steel and Zinc-Rich Prepainted Steel to Prior Strain


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1989 SAE Automotive Corrosion and Prevention Conference and Exposition ; 1989



    Erscheinungsdatum :

    01.12.1989




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Prepainted steel for body parts

    Pietersen, C.A. / Kuyk, C. / Hurkmans, A. | Tema Archiv | 1992


    Prepainted steel for body parts

    Pietersen,C.A. / Kuyk,C. / Hurkmans,A. et al. | Kraftfahrwesen | 1992


    Prepainted steel for automotive application

    Dubey, B.K. | Tema Archiv | 1988


    Corrosion performance and fuel compatibility of prepainted zinc-nickel coated steel for fuel tank applications

    Hahn,H.N. / Fountoulakis,S.G. / Ogonowski,T. et al. | Kraftfahrwesen | 1997