The influence of residual stress and retained austenite on the fracture behavior of bend test specimens of carburized steels was evaluated. The test results are part of an ongoing research effort intended to compare the relative fracture properties of alternate grades of steel and their respective standard grades having similar hardenability. In general, steels of equal hardenability and core carbon content exhibited similar fracture behavior. Compressive residual stress in the carburized case was found to significantly influence the impact fracture stress which, in turn, was correlated with impact fatigue properties. High levels of retained austenite at the surface caused the peak compressive residual stress to occur further into the case. The occurrence of residual stress peaks further into the case was not necessarily detrimental to impact fracture stress or impact fatigue properties. High-cycle fatigue limits were more dependent on processing variables than on differences in alloy content.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High-Cycle and Impact Fatigue Behavior of Carburized Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1978 SAE International Off-Highway and Powerplant Congress and Exposition ; 1978



    Erscheinungsdatum :

    01.02.1978




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High-cycle and impact fatigue behaviour of carburized steels

    Diesburg,D.E. / Climax Molybdenum,Ann Arbor,US | Kraftfahrwesen | 1978



    Bending fatigue performance of carburized gear steels

    Sieber,R. / Rockwell International,US | Kraftfahrwesen | 1992


    Bending Fatigue Performance of Carburized Gear Steels

    Sieber, Ray | SAE Technical Papers | 1992


    Bending Fatigue Performance of Gas- and Plasma-Carburized Steels

    Cornelissen, Bastiaan E. / Gondesen, Brigitte / Matlock, David K. et al. | SAE Technical Papers | 1999