Fatigue behavior of dissimilar ultrasonic spot welds in lap-shear specimens of magnesium AZ31B-H24 and hot-dipped-galvanized mild steel sheets is investigated based on experimental observations, closed-form stress intensity factor solutions, and a fatigue life estimation model. Fatigue tests were conducted under different load ranges with two load ratios of 0.1 and 0.2. Optical micrographs of the welds after the tests were examined to understand the failure modes of the welds. The micrographs show that the welds mainly fail from kinked fatigue cracks growing through the magnesium sheets. The optical micrographs also indicate that failure mode changes from the partial nugget pullout mode under low-cycle loading conditions to the transverse crack growth mode under high-cycle loading conditions. The closed-form stress intensity factor solutions at the critical locations of the welds are used to explain the locations of fatigue crack initiation and growth. A structural stress model based on the closed-form structural solution and the stress-life data for magnesium sheets is adopted to estimate the fatigue lives due to kinked crack growth. The fatigue live estimations based on the structural stress model are lower than the experimental results under high load ranges and are in better agreement with the experimental results under low load ranges.
Fatigue Behavior of Dissimilar Ultrasonic Spot Welds in Lap-Shear Specimens of Magnesium and Steel Sheets
Sae Int. J. Mater. Manuf
Sae International Journal of Materials and Manufacturing
SAE 2011 World Congress & Exhibition ; 2011
Sae International Journal of Materials and Manufacturing ; 4 , 1 ; 581-588
2011-04-12
8 pages
Aufsatz (Konferenz)
Englisch
Fatigue Behavior of Dissimilar 5754/7075 and 7075/5754 Spot Friction Welds in Lap-Shear Specimens
SAE Technical Papers | 2010
|