As the automotive industry becomes more concerned with the crash performance of automobiles, the behavior of used vehicles becomes an interesting subject. In this work, the effect of aging on spot welded joints was simulated by applying fatigue loading to the samples. Samples were then subjected to quasi-static and impact tests to measure the effect of fatigue aging to the strength of the samples. The results show (a) a reduction in the strength of the test samples under impact conditions, (b) no obvious reduction in quasi-static conditions, and (c) significant reduction in strength if cracks in the welds were initiated during the fatigue aging process.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Quasi-Static and Impact Strength of Fatigue Damaged Spot Welds


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Martinez, A. (Autor:in) / Miller, Kenneth W. (Autor:in) / Wang, P. C. (Autor:in) / Liu, S. (Autor:in) / Zhu, X. (Autor:in) / Chao, Y. J. (Autor:in)

    Kongress:

    SAE 2003 World Congress & Exhibition ; 2003



    Erscheinungsdatum :

    03.03.2003




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Quasi-static and impact strength of fatigue damaged spot welds

    Miller,K.W. / Chao,Y.J. / Martinez,A. et al. | Kraftfahrwesen | 2003


    Fatigue of Advanced High Strength Steel Spot-Welds

    Khosrovaneh, A. K. / Yan, Benda / Agrawal, Hari et al. | SAE Technical Papers | 2006


    Fatigue of advanced high strength steel spot-welds

    Bonnen,J.J. / Agrawal,H. / Amaya,M.A. et al. | Kraftfahrwesen | 2006



    Fatigue strength of spot welds in titanium-bearing HSLA-steels

    Pollard,B. / Jones and Laughlin Steel,Pittsburgh,US | Kraftfahrwesen | 1982