This study looked at the effects of cold deformation, sample orientation, and artificial aging (paint cure simulation) after forming on the tensile properties of 6009 aluminum sheet of two thicknesses, 0.035 in (0.889 mm) and 0.071 in (1.80 mm). Three modes of deformation were imposed; cold rolling, simple tension, and die compression.Test results indicated that the post-formed tensile properties were strongly influenced by deformation mode, sample orientation, sheet thickness, and artificial aging. Die compression produced tensile strengths of 67± 4 ksi (462± 28 MPa); by contrast cold rolled samples tested parallel to the rolling direction had tensile strengths of 31± 3 ksi (213± 21 MPa). Artificial aging increased strength in all deformation modes and exacerbated the deformation mode anisotropy of strength values.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Influences of Deformation Mode and Heat Treatment on Post-Formed Tensile Properties of 6009 Aluminum Sheet


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Piehler, H. R. (Autor:in) / Bogan, R. S. (Autor:in)

    Kongress:

    Passenger Car Meeting & Exposition ; 1980



    Erscheinungsdatum :

    1980-06-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The Influence of Deformation Mode and Heat Treatment on Post-Formed Tensile Properties of 6009 Aluminum Sheet

    Bogan,R.S. / Piehler,H.R. / Univ.Carnegie-Mellon,US et al. | Kraftfahrwesen | 1980


    Joining of Aluminum Alloys 6009/6010

    Hoch, F. R. | SAE Technical Papers | 1978


    Joining of Aluminium Alloys 6009/6010

    Hoch,F.R. / Aluminium Company of America,US | Kraftfahrwesen | 1978



    AIAA-2006-6009 Experimental Determination of the Effect of Rifling Grooves on the Aerodynamics of Small Caliber Projectiles

    Silton, S. / Webb, D. / American Institute of Aeronautics and Astronautics | British Library Conference Proceedings | 2006