Abstract This paper shows results of weldability testing of fine-grained high-strength low-alloy S460N steel welded in water environment by covered electrodes. The tests were carried out by using the CTS test specimens with fillet welds. Four specimens were welded under water and one specimen in air. Welded joints were subjected to non-destructive visual and penetration tests. The accepted joints were then subjected to macroscopic and microscopic inspection and Vickers hardness measurements as well. The experiments showed that S460N steel welded in water environment is characterized by a high susceptibility to cold cracking.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Cold Cracking of S460N Steel Welded in Water Environment


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Unbekannt


    Klassifikation :

    BKL:    50.92 Meerestechnik / 55.40 Schiffstechnik, Schiffbau



    Cold Cracking of S460N Steel Welded in Water Environment

    Tomków Jacek / Łabanowski Jerzy / Fydrych Dariusz et al. | DOAJ | 2018

    Freier Zugriff

    Effects of water temperature on cracking of wet-welded carbon steel

    West, T.C. / Mitchell, W.E. / Murray, R.I. | Tema Archiv | 1996