Abstract The polymerization of silica in water solution to form quartz fibers proceeds by a dehydration process, analogous to condensation polymerization in organic high-polymers, in which monomeric Si(OH)4 groups unite through Si−O−Si bonds with the elimination of $ H_{2} $O. The resulting fibers are structurally polar along the direction of elongation, are enantiomorphous, and generally shown stereospecific twisting around the direction of elongation. In these regards the fibers are analogues of biopolymers such as RNA and DNA. Quartz also possesses specific adsorptive relations to a wide range of organic substances including monomer amino acids, short-chain polypeptides, and proteins. These involve hydrogen-bonding between (OH) or silanoi groups on the surface of the quartz with active side-groups on the organic molecules and in part are epitaxial through dimensional coincidences in the interface. Geochemical evidence indicates that quartz was deposited in the early Precambrian ocean either by direct crystallization from seawater or by recrystallization of amorphous silica. What is of interest is the possible role of quartz fibers as a template and co-polymer in the passage of biomonomers in the pre-biotic ocean to the long-chain biopolymers such as nucleic acids and proteins that are involved in life processes.
Quartz fibers as templates for biopolymers
Origins of life ; 9 , 1 ; 17-25
1978
Aufsatz (Zeitschrift)
Englisch
BKL: | 44.71 Verkehrsmedizin | |
Lokalklassifikation TIB: | 535/3908/4290 |
SBS Phase Conjugation In Multimode Quartz Fibers
IEEE | 1997
|Online Contents | 1976
|Biopolymers suitable for space environments
SPIE | 2014
|Biopolymers for Medical and Pharmaceutical Applications
British Library Online Contents | 2006
|Permanent modification of fibrous materials with biopolymers
Kraftfahrwesen | 1999
|