A new method for calculating energy release rate (ERR) at the interface of concrete overlaid pavements is proposed using crack closure and the nodal force technique. This method transforms a 3D pavement system into a 2D interfacial crack model via a theoretical conversion. The interfacial ERRs of steel fibre-reinforced, roller-compacted, polymer-modified concrete overlay pavement subjected to vehicular load were calculated and compared with the measured interfacial fracture toughness of the bi-material. It was found that the ERRs considerably decrease with the increase in overlay thickness and elastic modulus of foundation. Thin overlays (less than 100 mm) should not be considered in overlay pavement design to avoid interfacial delamination induced by heavy vehicular loading. For a typical overlay pavement system subjected to complex vehicular loads, an interfacial crack suffers mainly from damage due to mode-I, opening, compared to mode-II, sliding, while mode-III, tearing damage is negligible.
Strain energy release rate at interface of concrete overlaid pavements
2017
Aufsatz (Zeitschrift)
Englisch
Pavement design , Fracture toughness , interface fracture , Concrete overlay pavement , Reinforcing steels , Modulus of elasticity , Fiber reinforced concretes , Tearing , Fiber reinforced polymers , Pavements , Two dimensional models , strain energy release rate , Energy release rate , Strain energy release rate , Crack closure
Interface Shear Stress in Overlaid Concrete Pavements
Online Contents | 1994
|Interface Shear Stress in Overlaid Concrete Pavements
British Library Online Contents | 1994
|Backcalculation of Asphalt-Overlaid Concrete Pavements
British Library Conference Proceedings | 1997
|Deterioration Modeling for Unlaid and Overlaid Pavements
Transportation Research Record | 2019
|