Thermal barrier coatings (TBCs) are ceramic coatings used in gas turbines to lower the base metal temperature. During operation, the TBC may fail through, for example, fatigue. In this study, a TBC system deposited on a Ni-base alloy was tested in tensile bending fatigue. The TBC system was tested as-sprayed and oxidized, and two load levels were used. After interrupting the tests, at 10,000–50,000 cycles, the TBC tested at the lower load had extensive delamination damage, whereas the TBC tested at the higher load was relatively undamaged. At the higher load, the TBC formed vertical cracks which relieved the stresses in the TBC and retarded delamination damage. A finite element (FE) analysis was used to establish a likely vertical crack configuration (spacing and depth), and it could be confirmed that the corresponding stress drop in the TBC should prohibit delamination damage at the higher load.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Bending Fatigue of Thermal Barrier Coatings




    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    52.30 / 52.52 / 52.52 Thermische Energieerzeugung, Wärmetechnik / 52.30 Strömungskraftmaschinen, Turbomaschinen



    Low-cycle fatigue of thermal-barrier coatings at 982° C

    Kaufmann, Albert / Liebert, Curt H. / Nachtigall, Alfred J. | TIBKAT | 1978


    Thermal Barrier Coatings

    Shih, Tom I-P. / Yang, Vigor | AIAA | 2014


    Thick thermal barrier coatings

    Larson,H.J. / Caterpillar Tractor,US | Kraftfahrwesen | 1991


    Thick thermal barrier coatings

    Yonushonis,T.M. / Ng,H.K. / Vovak,R.C. et al. | Kraftfahrwesen | 1991


    Thick Thermal Barrier Coatings

    Beardsley, M. D. / SAE / United States; Department of Energy; Office of Transportation Technologies | British Library Conference Proceedings | 1994