Since its introduction in 2003, alloy 718PlusTM spurred a lot of interest owing to its increased maximum service temperature over conventional Inconel 718 (704 °C versus 650 °C), good formability, and weldability together with its moderate cost. Understanding the high-temperature deformation characteristics and microstructural evolution is still of interest to many. It is known that the service performance and hot-flow behavior of this alloy are a strong function of the microstructure, particularly the grain size. To develop precise microstructure evolution models and foresee the final microstructure, it is important to understand how and under which forming conditions softening and precipitation processes occur concurrently. In this work, the softening behavior, its mechanisms, and the precipitation characteristics of 718PlusTM were investigated in two parallel studies. While cylindrical compression tests were employed to observe the hot-flow behavior, the precipitation behavior and other microstructural phenomena such as particle coarsening were tracked via hardness measurements. A precipitation–temperature–time (PTT) diagram was reported, and modeling of the flow curves via hyperbolic sine model was discussed in the light of the PTT behavior. Both “apparent” approach and “physically based” approach are implemented and two different sets of parameters were reported for the latter. Finally, recovery and recrystallization kinetics are described via Estrin–Mecking and Bergstrom, and Avrami kinetics, respectively.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High-Temperature Deformation of Inconel 718PlusTM




    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    52.52 Thermische Energieerzeugung, Wärmetechnik / 52.30 Strömungskraftmaschinen, Turbomaschinen / 52.52 / 52.30



    High Temperature Deformation of Inconel 718PlusTM

    Ozturk, Utkudeniz | Online Contents | 2016


    Modeling subsurface deformation induced by machining of Inconel 718

    Agmell, M. / Ahadi, A. / Zhou, J. M. et al. | British Library Online Contents | 2017



    Fundamental aging effects influencing high-temperature properties of solution-treated inconel X

    Frey, D.N. / Freemand, J.W. / White, A.E. | Engineering Index Backfile | 1951


    Dynamic High Temperature and Pressure Characterization of an Inconel Honeycomb Impact Attenuator

    Sly, Jacqueline R. / Maghsoudi, Elham / Pauken, Michael et al. | AIAA | 2018