Performance differences between bare 17-4PH steel V103 profile (NACA 6505 with rounded leading edge (LE) and trailing edge (TE)) gas turbine engine axial compressor blades, and those coated with either a chromium-aluminum-titanium nitride (CrAlTiN) or a titanium-aluminum nitride (TixAl1−xN) erosion-resistant coating were tested. A coating thickness of 16 μm was used, based on experimental results in the literature. Coatings were applied using arc physical vapor deposition at the National Research Council of Canada (NRC). All blades were tested under identical operating conditions in the Royal Military College of Canada (RMC) turbomachinery erosion rig. Based on a realism factor (RF) defined by the authors, this experimental rig was determined to provide the best known approximation to actual compressor blade erosion in aircraft gas turbine engine axial compressors. An average brown-out erosive media concentration of 4.9 g/m3 of air was used during testing. An overall defined Leithead–Allan–Zhao (LAZ) score metric, based on mass and blade dimension changes, compared the erosion-resistant performance of the bare and coated blades. Blade surface roughness data were also obtained. Based on the LAZ Score, CrAlTiN-coated blades performed at least 79% better than bare blades, and TixAl1−xN-coated blades performed at least 93% better than bare blades. The TixAl1−xN-coated blades performed at least 33% better than the CrAlTiN-coated blades. Extrapolation of results predicted that a V-22 Osprey tiltrotor military aircraft, for example, could fly up to 79 more missions with TixAl1−xN-coated compressor blades in brown-out sand concentrations than with uncoated blades.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Enhanced Experimental Testing of New Erosion-Resistant Compressor Blade Coatings




    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    52.52 Thermische Energieerzeugung, Wärmetechnik / 52.30 Strömungskraftmaschinen, Turbomaschinen / 52.52 / 52.30




    Gas Turbine Aero Engine Compressor Blade Erosion and Heat Resistant Coatings

    Savkov, K. / Doroshko, S. / Urbaha, M. et al. | British Library Conference Proceedings | 2011


    Gas Turbine Aero Engine Compressor Blade Erosion and Heat Resistant Coatings

    Savkov, K. / Doroshko, S. / Urbaha, M. et al. | British Library Conference Proceedings | 2011


    Erosion- and corrosion-resistant coatings for aircraft compressor blades

    Swadzba, L. / Formanek, B. / Gabriel, H.M. et al. | Tema Archiv | 1993


    Erosion resistant blade and blade coating

    KUMAR RAJESH S / BARTH ROBERT A / SCHMIDT WAYDE R | Europäisches Patentamt | 2019