Thermomechanical fatigue (TMF) crack growth modeling has been conducted on Inconel 718 with dwell time at maximum load. A history dependent damage model taking dwell damage into account, developed under isothermal conditions, has been extended for TMF conditions. Parameter determination for the model is carried out on isothermal load controlled tests at 550–650 °C for surface cracks, which later have been used to extrapolate parameters used for TMF crack growth. Further, validation of the developed model is conducted on a notched specimen subjected to strain control at 50–550 °C. Satisfying results are gained within reasonable scatter level compared for test and simulated number of cycles to failure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Thermomechanical fatigue crack growth modeling in a ni-based superalloy subjected to sustained load




    Erscheinungsdatum :

    2016



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    52.30 / 52.52 / 52.52 Thermische Energieerzeugung, Wärmetechnik / 52.30 Strömungskraftmaschinen, Turbomaschinen