We present bulk heterojunction organic solar cells fabricated by spray‐casting both the PEDOT:PSS hole‐transport layer (HTL) and active PBDTTT‐EFT:PC 71 BM layers in air. Devices were fabricated in a (6 × 6) array across a large‐area substrate (25 cm 2 ) with each pixel having an active area of 6.45 mm 2 . We show that the film uniformity and operational homogeneity of the devices are excellent. The champion device with spray cast active layer on spin cast PEDOT:PSS had an power conversion efficiency (PCE) of 8.75%, and the best device with spray cast active layer and PEDOT:PSS had a PCE of 8.06%. The impacts of air and light exposure of the active layer on device performance are investigated and found to be detrimental. Copyright © 2015 John Wiley & Sons, Ltd. High efficiency arrays of polymer solar cells are fabricated by spray‐coating the photoactive and/or PEDOT:PSS layers in air. Devices were fabricated in a 6 × 6 array across a 5 × 5 cm 2 substrate with each pixel having an active area of 6.45 mm 2 . The champion device with spray cast active layer on spin cast PEDOT:PSS had a PCE of 8.75%, and the best device with spray cast active layer and PEDOT:PSS had a PCE of 8.06%.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High efficiency arrays of polymer solar cells fabricated by spray‐coating in air



    Erschienen in:

    Progress in photovoltaics ; 24 , 3 ; 275-282


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher