A conversion coating of iron and copper was investigated with the purpose of increasing the performance of Sanergy HT as a potential SOFC interconnect material. Samples were exposed to a simulated cathode atmosphere (air, 3 % H2O) for durations of up to 1000 h at 850 °C. Their performance in terms of corrosion, chromium evaporation and electrical resistance (ASR) was monitored and compared to uncoated and cobalt-coated Sanergy HT samples. The copper iron coating had no negative effects on corrosion protection and decreased chromium evaporation by about 80%. An Area Specific Resistance (ASR) of 10 mΩcm2 was reached after 1000 h of exposure. Scanning Electron Microscopy revealed well adherent oxide layers comprised of an inner chromia layer and an outer spinel oxide layer.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Copper Iron Conversion Coating for Solid Oxide Fuel Cell Interconnects



    Erschienen in:

    Erscheinungsdatum :

    2015




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    Lokalklassifikation TIB:    645/5625
    BKL:    52.57 Energiespeicherung / 53.36 Energiedirektumwandler, elektrische Energiespeicher