This study analyzed the effect of various semiconductors of transition metal oxides in modified lithiated NiO on the electrochemical performance of a single layer fuel cell (SLFC). A typical ionic conductor Ce0.8Sm0.2O2-δ (SDC) and three types of semiconductors Li0.3Ni0.6Cu0.07Sr0.03O2-δ (LNCuS), Li0.3Ni0.6Mn0.07Sr0.03O2-δ (LNMnS) and Li0.3Ni0.6Co0.07Sr0.03O2-δ (LNCoS), were the fundamental components of the SLFCs. The components were characterized by using X-ray diffraction (XRD), a scanning electron microscope (SEM), and an energy-dispersive X-ray spectrometer (EDS). The stability of the synthesized materials was evaluated using thermal gravity analysis (TGA). The ohmic resistances at 500 °C were 0.36, 0.48 and 0.58 Ω cm2 for 6SDC-4LNMnS, 6SDC-4LNCoS and 6SDC-4LNCuS, respectively. Among the three SLFCs, the single cell with 6SDC-4LNMnS achieves the highest power density (422 mW cm-2) but the lowest temperature stability, while the single cell with 6SDC-4LNCuS achieved the lowest power density (331 mW cm-2) but the highest temperature stability during the operation temperature.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Electrochemical study of lithiated transition metal oxide composite for single layer fuel cell



    Erschienen in:

    Erscheinungsdatum :

    2015




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    Lokalklassifikation TIB:    645/5625
    BKL:    52.57 Energiespeicherung / 53.36 Energiedirektumwandler, elektrische Energiespeicher




    Lithiated Transition Metal Oxide Cathodes in Molten Nitrate Electrolytes for Lithium Thermal Batteries

    Briscoe, J. Douglass / Castro, L. Gabriel | SAE Technical Papers | 2002


    lithiated FeF

    Fan, Xiulin | Online Contents | 2016



    Lithiated Natural Graphite in Lithium-Ion Cell

    Libich, J. / Sedlařiková, M. / Vondrák, J. et al. | TIBKAT | 2017

    Freier Zugriff