SiN x : Tb 3+-Yb 3+, an efficient down-conversion layer compatible with silicon solar cell process Abstract Tb 3+-Yb 3+ co-doped SiN x down-conversion layers compatible with silicon Photovoltaic Technology were prepared by reactive magnetron co-sputtering. Efficient sensitization of Tb 3+ ions through a SiN x host matrix and cooperative energy transfer between Tb 3+ and Yb 3+ ions were evidenced as driving mechanisms of the down-conversion process. In this paper, the film composition and microstructure are investigated alongside their optical properties, with the aim of maximizing the rare earth ions incorporation and emission efficiency. An optimized layer achieving the highest Yb 3+ emission intensity was obtained by reactive magnetron co-sputtering in a nitride rich atmosphere for 1.2 W/cm{}^2 and 0.15 W/cm{}^2 power density applied on the Tb and Yb targets, respectively. It was determined that depositing at 200 {\textdegree}C and annealing at 850 {\textdegree}C leads to comparable Yb 3+ emission intensity than depositing at 500 {\textdegree}C and annealing at 600 {\textdegree}C, which is promising for applications toward silicon solar cells.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    SiNx:Tb3+–Yb3+, an efficient down-conversion layer compatible with a silicon solar cell process




    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher / 52.52 Thermische Energieerzeugung, Wärmetechnik / 52.56 Regenerative Energieformen, alternative Energieformen / 50.70 Energie: Allgemeines




    Silicon IC compatible LIGA mask-fabrication process

    Suzuki, K. / Sugiyama, S. | British Library Online Contents | 1997



    CMOS-compatible process for fibre alignment grooves in silicon

    Chaffey, J. / Austin, M. / Switala, I. et al. | IEEE | 2002