We report on a photolithographic and electro‐deposition process that results in an optimized front grid structure for high efficiency multi‐junction III–V concentrator solar cells operating under flux concentrations up to 1000 suns. Two different thick photoresists were investigated to achieve a 6 µm wide grid line with an aspect ratio of 1:1. A positive photoresist, SPR220 manufactured by Rohm and Haas was compared with a negative photoresist, nXT15 manufactured by AZ. A gold sulfite electrolyte was employed to prevent underplating as well as for environmental and safety considerations. An initial layer of nickel was discovered to be necessary to prevent delamination of the fingers during the removal of the contact layer. When deposited on a purpose grown, heavily doped GaAs contact layer, this Ni/Au contact exhibits an acceptable specific contact resistance in the low 10 −4 to mid 10 −5 Ohm cm 2 range along with excellent adhesion without sintering. Copyright © 2014 John Wiley & Sons, Ltd. We report on a photolithographic and electro‐deposition process that results in an optimized front grid structure for high efficiency multi‐junction III–V concentrator solar cells operating under flux concentrations in excess of 1000 suns. When deposited on a purpose grown, heavily doped GaAs contact layer, this Ni/Au contact exhibits a low specific contact resistance of 10 −4 Ohm cm 2 and excellent adhesion without sintering.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High aspect ratio electrodeposited Ni/Au contacts for GaAs‐based III–V concentrator solar cells



    Erschienen in:

    Progress in photovoltaics ; 23 , 5 ; 646-653


    Erscheinungsdatum :

    2015




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher




    Thermal annealing of GaAs concentrator solar cells

    Curtis, H.B. / Brinker, D.J. | Tema Archiv | 1989


    Characteristics of GaAs-based concentrator cells

    Araki, Kenji | Online Contents | 2001


    Space Concentrator Solar Cells Based on Multilayer LPE Grown AlGaAs/GaAs Heterostructure

    Khvostikov, V. P. / Larionov, V. R. / Paleeva, E. V. et al. | British Library Conference Proceedings | 1995


    Space Concentrator Solar Cells Based on Multilayer LPE Grown AlGaAs/GaAs Heterostructure

    Khvostikov, V. P. / Larionov, V. R. / Paleeva, E. V. et al. | British Library Online Contents | 1995