Superstrate solar cells were prepared by thermal evaporation of Cu(In,Ga)Se2 onto ZnO coated glass substrates. For the first time, photo‐conversion efficiencies above 11% were reached without the necessity of additional light soaking or forward biasing of the solar cell. This was achieved by modifying the deposition process as well as the sodium doping. Limitations of the superstrate device configuration and possible ways to overcome these were investigated by analyzing the hetero‐interface with electron microscopy and X‐ray photoemission spectroscopy measurements, combined with capacitance spectroscopy and device simulations. A device model was derived that explains how on the one hand the GaO x , which forms at the CIGSe/ZnO interface, reduces the interface recombination. On the other hand how it limits the efficiency by acting as an electron barrier at the hetero‐interface presumably because of a high density of negatively charged acceptor states like Cu Ga . The addition of sodium enhances the p‐type doping of the absorber but also increases the net doping within the GaO x . Hence, a trade‐off between these two effects is required. The conversion efficiency was found to decrease over time, which can be explained in our model by field‐induced diffusion of sodium cations out from the GaO x layer. The proposed device model is able to explain various effects frequently observed upon light soaking and forward biasing of superstrate devices. Copyright © 2014 John Wiley & Sons, Ltd. Cu(In,Ga)Se2 superstrate solar cells were prepared by thermal evaporation of the absorber material onto ZnO coated glass substrates. For the first time, photo‐conversion efficiencies above 11% were reached without light soaking or forward biasing of the solar cell. Limitations and possible ways to overcome these were investigated by analyzing the hetero‐interface with electron microscopy and XPS measurements, combined with capacitance spectroscopy and device simulations. A device model is proposed to explain the effects of light soaking and forward biasing of superstrate devices.
Cu(In,Ga)Se2 superstrate solar cells: prospects and limitations
Progress in photovoltaics ; 23 , 10
2015
Aufsatz (Zeitschrift)
Englisch
SCAPS , ZnO , sodium , superstrate , CIGSe , tandem , capacitance
BKL: | 53.36 Energiedirektumwandler, elektrische Energiespeicher |
CuSe2 superstrate solar cells: prospects and limitations
Online Contents | 2015
|Substrate versus superstrate configuration for stable thin film silicon solar cells
Online Contents | 2013
|Advantageous light management in Cu(In,Ga)Se2 superstrate solar cells
Online Contents | 2016
|Preparation of CuInSe2 films on large grain CdS films for superstrate-type solar cells
Online Contents | 1995
|Optical properties of silicon-based thin-film solar cells in substrate and superstrate configuration
Online Contents | 2002
|