An L-shaped curved beam specimen and a tension loading fixture were proposed to measure the interlaminar tension strength of laminated and textile composites. The specimen size was 2 X 2 in. (51 X 51 mm). The use of a standard tension test machine and the introduction of load nearly at the specimen midthickness were the advantages of the proposed specimen. Modified Lekhnitskii and beam theory equations for calculating interlaminar stresses of an L-beam were verified by finite element analysis. The beam theory equation is simple and accurate for mean radius to thickness ratios greater than 1.5. The modified Lekhnitskii equations can be used for detailed stress field calculation. AS4/3501-6 graphite/epoxy unidirectional specimens with thicknesses of 16, 24, and 32 piles were fabricated and tested. The delamination initiation site agreed with the calculated maximum interlaminar tension stress location for all three thicknesses. Average interlaminar tension strengths of 16-, 24-, and 32-ply laminates were 47.6, 40.9, and 23.4 MPa, respectively.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Interlaminar tension strength of graphite/epoxy composite laminates


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    1994-07-01



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Interlaminar tension strength of graphite/epoxy composite laminates

    Shivakumar, Kunigal N. / Allen, Harold G. / Avva, Vishnu S. | AIAA | 1994