Addition of some rare-earth oxides to prior alumina (only) coating material increases maximum service temperature of palladium/chromium-wire strain gauges. Pd/Cr wires used at temperatures up to 800 degrees C without excessive drift in electrical resistance. Oxides used: zirconia (ZrO2), yttria (Y2O3), ceria (CeO2), and hafnia (HfO2). Addition of one of these oxides to decrease oxidation of wire at high temperature. Protection against oxidation increases with concentration of rare-earth oxide. Addition of ZrO2 at 4 to 6 weight percent or Y2O3 at 1 weight percent results in smallest drift in electrical resistance.
Protective Coats For High-Temperature Strain Gauges
NASA Tech Briefs ; 17 , 9
1993-09-01
Sonstige
Keine Angabe
Englisch
High-Temperature Resistance Strain Gauges
NTRS | 1994
|More About High-Temperature Resistance Strain Gauges
NTRS | 1994
|More About High-Temperature Resistance Strain Gauges
Online Contents | 1994
Protective Coats For Zinc-Rich Primers
NTRS | 1993
|Diamondlike Protective Coats For Infrared Windows
NTRS | 1992
|