Rejuvenating treatments demonstrated. Experiments with three alloys show some combinations of heat treatment, hot isostatic pressing, and/or surface treatment extends cycle lives of fatigue-damaged or fatigue-precracked specimens. For each alloy, tests were first done to determine "baseline" high-cycle-fatigue lives and high-cycle-fatigue failure modes over range of test conditions. Controlled fatigue damage introduced into specimens. Damaged specimens subjected to candidate rejuvenating treatments, then tested to failure. Effectiveness of each treatment judged by comparing fatigue data of damaged and treated specimens to "baseline" fatigue and data taken at same test conditions.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Extending Fatigue Lives Of Selected Alloys


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    1988-05-01



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Chronic fatigue endangers lives

    Online Contents | 1997



    Bayesian Estimations of Fatigue Lives

    Kovacs, K. | British Library Conference Proceedings | 2008


    Fatigue Lives Of Laser-Cut Metals

    Martin, Michael R. | NTRS | 1988


    Increasing Fatigue Lives of Laser-Cut Parts

    Glick, Edward W. / Donovan, Michael H. | NTRS | 1987