Process changes iterated under guidance of x-radiography. In recent work at NASA Lewis Research Center, density gradients in sintered silicon nitride, characterized by x-radiography, identified and appeared strongly dependent upon powder-processing and sintering conditions. NASA technical memorandum describes systematic investigation, based upon preliminary work, of density-gradient/flexural-strength relationships as affected by processing.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Optimization of Processing of Si3N4


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    1988-01-01



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Interphase optimization of SiCf/Si3N4 composites

    DENG Yangfang / CHEN Xu / WANG Tongtong et al. | DOAJ | 2023

    Freier Zugriff

    Grinding Si3N4 Powder In Si3N4 Equipment

    Herbell, Thomas P. / Freedman, Marc R. / Kiser, James D. | NTRS | 1989


    Processing of hot isostatic pressed Si3N4-components

    Boehmer,M. / Heinrich,J. / Hoechst CeramTec,Selb,DE et al. | Kraftfahrwesen | 1986


    Robust Design Optimization of High Temperature SiC-Si3N4 Nanocomposites

    Mejía-Rodríguez, Gilberto / Renaud, John | AIAA | 2010


    SiC-Si3N4 gradient composite ceramics by special HIP processing

    Dongliang,J. / Jihong,S. / Shouhong,T. et al. | Kraftfahrwesen | 1991