Failure mechanisms observed using transparent fiberglass/epoxy birefringent materials. Technique based on use of transparent fiberglass/epoxy birefringent material. Transparency allows visual observation of location of initial laminate failure and of subsequent failure propagation; birefringence allows laminate stress distribution to be observed during test and also after test if permanent residual stresses occur. Nondestructive technique developed to observe failure as it develops and as propagates within laminate.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Compression-Failure Mechanisms in Composite Laminates


    Beteiligte:
    Shuart, M. J. (Autor:in) / Williams, J. G. (Autor:in) / Cooper, P. A. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1986-05-01



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :





    Failure Mechanisms of Composite Laminates with Embedded Ply Waviness under Tension

    Gonzalez Ayala, Gabriela / Heise, Jarod / Diaz Montiel, Paulina et al. | AIAA | 2024


    Failure analysis for composite laminates

    TENNYSON, R. / ELLIOTT, G. / MABSON, G. et al. | AIAA | 1984