Insoluble, even coating formed by soaking in polyacrylic acid. Carbon fiber material prepared by soaking in solution of 20 percent polyacrylic acid in water. Material blotted and dried at 120 degrees C for at least 2 hours. Dried material reacted with boiling aqueous solution of calcium acetate. Treated material removed from boiling solution, blotted, dried at 120 degrees C, washed with distilled water, and dried again.
Binder for Carbon-Fiber Coating
NASA Tech Briefs ; 8 , 2
1984-11-01
Sonstige
Keine Angabe
Englisch
ALUMINUM COATING, CORROSION AND HEAT RESISTANT Thermosetting, Inorganic Binder
SAE Technical Papers | 1971
ALUMINUM COATING MATERIAL, CORROSION AND HEAT RESISTANT Thermosetting, Inorganic Binder
SAE Technical Papers | 1978
Aluminum Coating Material, Corrosion and Heat Resistant Thermosetting, Inorganic Binder
SAE Technical Papers | 2008
Tungsten Disulfide Coating, Thin Lubricating Film, Binder-Less Impingement Applied
SAE Technical Papers | 2010
Tungsten Disulfide Coating, Thin Lubricating Film, Binder-Less Impingement Applied
SAE Technical Papers | 2019