A test program to investigate the deformation process observed in the hot gas wall of rocket thrust chambers was conducted using three different liner materials. Five thrust chambers were cycled to failure using hydrogen and oxygen as propellants at a chamber pressure of 4.14 MN/m square (600 psia). The deformation was observed nondestructively at midlife points and destructively after failure occurred. The cyclic life results are presented with an accompanying discussion about the types of failure encountered. Data indicating the deformation of the thrust chamber liner as cycles are accumulated are presented for each of the test thrust chambers.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Some effects of cyclic induced deformation in rocket thrust chambers


    Beteiligte:
    Hannum, N. P. (Autor:in) / Quentmeyer, R. J. (Autor:in)

    Kongress:

    Conf. on Advanced Technol. for Future Space Systems ; 1979 ; Hampton, VA, United States


    Erscheinungsdatum :

    01.01.1979


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Keine Angabe


    Sprache :

    Englisch




    Some effects of cyclic induced deformation in rocket thrust chambers

    HANNUM, N. / QUENTMEYER, R. / KASPER, H. | AIAA | 1979



    Some effects of cyclic induced deformation in rocket thrust chambers

    Hannum, N. P. / Quentmeyer, R. J. / Kasper, H. J. | NTRS | 1979