Internal pressure vessels were designed; the filament was wound of carbon fibers and epoxy resin and tested to burst. The fibers used were Thornel 400, Thornel 75, and Hercules HTS. Additional vessels with type A fiber were made. Polymeric linears were used, and all burst testing was done at room temperature. The objective was to produce vessels with the highest attainable PbV/W efficiencies. The type A vessels showed the highest average efficiency: 2.56 x 10 to the 6th power cm. Next highest efficiency was with Thornel 400 vessels: 2.21 x 10 to the 6th power cm. These values compare favorably with efficiency values from good quality S-glass vessels, but strains averaged 0.97% or less, which is less than 1/3 the strain of S-glass vessels.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Carbon fiber internal pressure vessels


    Beteiligte:
    Simon, R. A. (Autor:in)

    Erscheinungsdatum :

    17.07.1973


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Lighter weight fiber/metal pressure vessels using carbon overwrap

    MORRIS, E. / SEGIMOTO, M. / LYNN, V. | AIAA | 1986




    Carbon pressure vessels for gas storage

    REGAN WILLIAM RAYMOND / GRUNDMANN MICHAEL JASON / DEVAUL RICHARD WAYNE | Europäisches Patentamt | 2021

    Freier Zugriff