The objective of this program was to investigate chemical environment-load interaction effects on crack propagation. Dry air (<10 percent relative humidity) was used as a reference environment. Alternate immersion in synthetic sea water was used to simulate the aggressive chemical environment to which Navy carrier based aircraft are subjected. Tests were performed to determine the behavior of 300M and HP-9-4-.30 steel in both environments under a variety of stress ratios and load wave shapes. A crack growth prediction capability developed through analysis and test accounts for environment and load interaction effects. A flight-by-flight test stress history was developed for a landing gear of a carrier based Navy aircraft. Crack growth predictions were prepared and tests performed to verify the chemical environment-spectrum loading analysis capability. A comparison of landing gear spectra under Air Force and Navy design conditions is presented. (Author)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Environment-Load Interaction Effects on Crack Growth in Landing Gear Steels


    Beteiligte:
    C. R. Saff (Autor:in)

    Erscheinungsdatum :

    1980


    Format / Umfang :

    155 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch




    Landing gear, aircraft comprising landing gear and method of distributing load of landing gear

    BENJAMIN BISHOP | Europäisches Patentamt | 2023

    Freier Zugriff

    Detection of fatigue crack growth in aircraft landing gear

    Baxter, M.G. / Pullin, R. / Holford, K.M. | Tema Archiv | 2004


    Corrosion of Aircraft Landing Gear Steels

    Lee | Online Contents | 1994


    The Future of Landing Gear Steels

    Emerald Group Publishing | 1991


    LANDING LOAD MONITOR FOR AIRCRAFT LANDING GEAR

    YATES MICHAEL STUART / KEEN PHILLIP | Europäisches Patentamt | 2015

    Freier Zugriff