There is a clear need for the development of alternate repair methods which preclude having to drydock a ship. An area of ship repair which has the potential to accomplish this objective involves the use of underwater wet welding. Fatigue performance was evaluated by testing underwater wet butt welds fabricated in 3/8-inch ASTM A 36 steel, using E7014 Type electrodes. The underwater wet welds were fabricated in fresh water at a depth of 30 feet, using a wet welding procedure qualified to the standards of ANSI/AWS D3.6-89, for Type B welds. Fatigue testing was performed on transverse weld specimens, with and without backing bars, subjected to cyclic axial tensile loading.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Underwater Repair Procedures for Ship Hulls (Fatigue and Ductility of Underwater Wet Welds)


    Beteiligte:
    K. Grubbs (Autor:in) / C. Zanis (Autor:in)

    Erscheinungsdatum :

    1993


    Format / Umfang :

    88 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch




    Underwater Noise from Ship Hulls

    Andresen, K. / Royal Institution of Naval Architects | British Library Conference Proceedings | 1995



    Underwater Ship Repair

    N. M. Madatov | NTIS | 1970


    Underwater nondestructive testing of ship hull welds

    Youshaw, R. / Dyer, C. | Tema Archiv | 1979


    Underwater nondestructive testing of ship hull welds

    Youshaw, R. / Dyer, C. | TIBKAT | 1979