Ageing military aircraft fleets are becoming the norm as fleet managers try to extend operational life without compromising safety. This has led to substantial world-wide research into ageing aircraft and the implications of corrosion and multi-site damage on aircraft residual strength and fatigue life. This report details part of DSTO's research program into the effect of pitting corrosion on aircraft structural integrity. The report focuses on F/A-18 structural aluminium alloy and its susceptibility to developing large pits. The report emphasises that with the present design philosophies of Safe-Life and Damage Tolerance, the major corrosion problem areas on aircraft will be secondary structure or non-fracture critical structure. The report also shows the applicability of the Equivalent Crack Size approach to assessing corrosion. While the ECS approach needs further research, it appears to be, currently, the best approach to assessing pitting corrosion and its effect on aircraft structural integrity.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Equivalent Crack Size Modelling of Corrosion Pitting in an AA7050-T7451 Aluminium Alloy and its Implications for Aircraft Structural Integrity


    Beteiligte:
    B. R. Crawford (Autor:in) / R. K. Sharp (Autor:in)

    Erscheinungsdatum :

    2012


    Format / Umfang :

    91 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch





    e170226aFinal00067 SCATTER IN THE GROWTH OF SMALL CRACKS IN AA7050-T7451

    Huang, Pu / Barter, Simon / Jones, Rhys et al. | TIBKAT | 2018


    Probability Modelling of Corrosion Fatigue Crack Growth and Pitting Corrosion

    Wei, R. P. / Li, C. / Harlow, D. G. et al. | British Library Conference Proceedings | 1997


    Implications of Corrosion with respect to Aircraft Structural Integrity

    G. K. Cole / G. Clark / P. K. Sharp | NTIS | 1997


    Modelling of Fatigue Crack Growth from exfoliation and Pitting Corrosion

    Clark, G. / Sharp, P. K. / Mills, T. et al. | British Library Conference Proceedings | 2002