Four full-scale experiments were conducted at Sandia National Laboratories' rocket sled facility to provide data on the response of reinforced concrete containment walls to impact and penetration by postulated turbine-produced missiles. The missiles' mass, velocity, and attitude, and the steel liner thickness, were varied. A 1476-kg, 120 exp 0 segment cut from a shrunk-on turbine disc was used for three experiments, and a 2100-kg, 137 exp 0 segment of another disc was used for one experiment. The targets were concrete panels fabricated of commercial ready-mix concrete of strength 24 to 28 MPa at 28 days and heavily reinforced (approx. = 5% by volume) with No. 18 (57-mm-dai) bars. Impacts were perpendicular to the targets at their centers. Three impacts were with the sharp corner of the missile forward (piercing) and one was with the rounded side forward (blunt). Rebar strains, liner strains, and rear face kinematic quantities were recorded for each test. Internal pressure pulses generated by the impacts were recorded on two tests. High-speed camera coverage was extensive. Depth of penetration was the primary measure diameter. Penetration depths into the 1.37-m-thick panels ranged from 33 cm for the blunt impact of the 1476-kg missile at 92 m/s to 65 cm for the piercing impact of the 2100-kg missile at 115m/s. Impact at the piercing attitude caused significantly more severe rear face cracking than did impact at the blunt attitude, but since rear face panel displacements in excess of 6 cm and velocities greater than 7 m/s were measured, results suggested that impact at a blunt attitude might cause scabbing at lower velocities than impact at a piercing attidude. In these tests, the presence of a 9.5-mm-thick steel liner on the rear face of the panel in the latter two tests precluded scabbing. Results also indicated that design formulas in common use give conservative results. (ERA citation 08:023610)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Full-Scale Turbine-Missile Concrete Impact Experiments. Final Report


    Beteiligte:
    R. L. Woodfin (Autor:in)

    Erscheinungsdatum :

    1983


    Format / Umfang :

    159 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch