The research of the development kerosene soot carbon particles and its application as electrode for lithium ion battery has been done. The carbon was prepared from kerosene by using thermal plasma pyrolisis and characterized by Boehm titration in order to determine the carbon functional group, point zero charge for surface charge and X-ray diffraction for crystalography. Carbon was mixed with polianilin to form anode and mixed with lithium, iron salts and phosphate to form LiFePO4 as cathode. Both electrodes were fabricated into lithium ion battery with Li2SO4 as electrolyte. The performance of battery was measured with the variaton of electrolyte concentration i e., 0.1 M, 0.5 M, and 1 M. Boehm titration result showed that the carbon has acid functional groups greater than base functional group as 6.90 mgeq. 4.80 of point zero charge pH was in acid condition. The crystalography of carbon as anode presented in diffractogram showed 2θ = 23.68 and 42.33 of diffraction peaks and indicated graphite crystal in the carbon. CV measurement reveal that the oxidation occurred at the peak of anode current, i e., 0.015 A for 0.3 V whereas the reduction occured at the –0.3 V and 0.007 A. A Galvanostatic charge discharge measurenment showed that The highest capacity is obtained in 0.52 mAh/g with a voltage of 0.71 Volts, which is the 500th cycle. The lowest capacity is obtained in only 0.15 mAh/g of 0.2 Volts, that is in cycle 1st.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Preparation of Kerosene Soot Carbon Electrode and Its Application in Lithium Ion Battery


    Beteiligte:
    Syarif, Nirwan (Autor:in) / Rohendi, Dedi (Autor:in) / Prayogo, M. Ridho (Autor:in)


    Erscheinungsdatum :

    01.11.2019


    Format / Umfang :

    444596 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    PAH and Soot Formation within Kerosene Pyrolysis

    Slavinskaya, N. / Zizin, A. / Aigner, M. et al. | British Library Conference Proceedings | 2009


    Influence of Kerosene Preheating and Pyrolysis on the PAH and Soot Formation

    Slavinskaya, Nadezhda / Zizin, Anton / Aigner, Manfred | AIAA | 2009


    All-solid-state lithium ion battery negative electrode material, preparation method, battery and application

    HAN JUNWEI / YU HUIYU / KONG DEBIN et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    Analysis of Smoke-Aerosol Formation in Pressurized Turbulent Kerosene/Air Flames Using Different Soot Models

    Darbandi, Masoud / Ghafourizadeh, Majid / Saidi, Mohammad Hasan et al. | AIAA | 2017


    Lithium ion battery positive electrode slurry and preparation method and application thereof

    ZHU QING / LIU YONGFEI | Europäisches Patentamt | 2020

    Freier Zugriff