Eight encapsulants with operating temperatures up to 250°C were surveyed for use in planar packages for wide-bandgap dice. Two of the encapsulants failed processability test because they were not able to flow, and another two failed because they induced voids or cracks after curing. The dielectric results of the remaining four encapsulants showed that both dielectric strength and permittivity decreased almost 40% when the temperature was increased to 250°C. As the three encapsulants were used to encapsulate a power module, it was proven that all of them could protect the package from early breakdown caused by the poor dielectric strength of air. The thermal aging test showed that materials were hardened during the aging process, and cracking started in the material matrix. The dielectric strength of the sample would drop 60%–70% to only around 10 kV/mm once cracking occurred.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Assessment of encapsulants for high-voltage, high-temperature power electronic packaging


    Beteiligte:
    Yao, Yiying (Autor:in) / Lu, Guo-Quan (Autor:in) / Chen, Zheng (Autor:in) / Boroyevich, Dushan (Autor:in) / Ngo, Khai D. T. (Autor:in)


    Erscheinungsdatum :

    01.04.2011


    Format / Umfang :

    1706650 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Assessment of High-Temperature Encapsulants for Planar Packages

    Boroyevich, Dushan / Lu, Guo-quan / Seshadri, Jayashree et al. | SAE Technical Papers | 2010


    ENCAPSULANTS FOR WINDOW ASSEMBLIES

    BENNETT DANIEL | Europäisches Patentamt | 2015

    Freier Zugriff

    ENCAPSULANTS FOR WINDOW ASSEMBLIES

    BENNETT DANIEL | Europäisches Patentamt | 2017

    Freier Zugriff

    Encapsulants for window assemblies

    BENNETT DANIEL | Europäisches Patentamt | 2018

    Freier Zugriff

    New Environmentally Conscious Encapsulants

    Arris, H. W. / Wischmann, K. B. | British Library Conference Proceedings | 1994