The objective of this research is to investigate the comparison nanosilica and aluminium powder in epoxy as adhesive on shear strength of single lap joint between aluminium-GFRP composite. The shear strength was determined by utilizing the single-lap shear test. The nanosilica content was varied in 0, 1, 2, 3 and 4 (w/w), whereas the content of aluminium powder was varied in 15, 20, 25, 30 and 35 (w/w). Experimental results showed that the nanosilica-epoxy adhesive has the maximum shear strength at 2 % nanosilica content. However, for the use of the aluminium powder-epoxy adhesive, the shear strength decreased significantly along with elevated level of aluminium powder. The adhesive failure mode occurres the joining using nanosilica-epoxy as adhesive, and the joining using aluminium powder-epoxy as adhesive is categoried as cohesive failure mode. The cohesive failure mode has higher shear strength over adhesive failure mode.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Adhesive nanosilica/aluminium powder — Epoxy for joint application on composite car body of electrical vehicle




    Erscheinungsdatum :

    2013-11-01


    Format / Umfang :

    285948 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Mechanical Characterization of Nanosilica/Epoxy Nanocomposites

    Swaminathan, G. / Hossain, M. / Shivakumar, K. et al. | British Library Conference Proceedings | 2010


    Mechanical Characterization of Nanosilica/Epoxy Nanocomposites

    Swaminathan, Gowthaman / Hossain, Mohammad / Shivakumar, Kunigal | AIAA | 2010


    Structural adhesive for aluminium body

    Saito,A. / Sakakibara,T. / Okuri,Y. et al. | Kraftfahrwesen | 1992


    Adhesive bonding of aluminium automotive body sheet

    Alcoa Technical Center, Pa. | Kraftfahrwesen | 1975


    Adhesive bonding of aluminium automotive body sheet

    Minford,J.D. / Vader,E.M. / Alcoa | Kraftfahrwesen | 1974